440C Stainless Steel Plate

440C grade stainless steel is a kind of high carbon martensitic stainless steel. High strength, medium corrosion resistance, good hardness and wear resistance. Grade 440C achieves the highest strength, hardness and wear resistance of any stainless steel alloy after heat treatment. Its extremely high carbon content is the reason for these characteristics, which makes the 440C particularly suitable for applications such as ball bearings and valve parts.

Classification :

Stainless Steel Plate

+86-19963884193

sales01@szcnsteel.com

E-mail

440C Stainless Steel Plate Description

Product Parameters

Product Name	440C Stainless Steel Plate
Type	Plate
Thickness	0.3mm-200mm
Length	2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc.
Width	40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc.
Standard	ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface	BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc.
Scope of Application	Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc.
Certificate	ISO, SGS, BV, etc.
Production Technology	Hot Rolling, Cold Rolling
Edge Processing	Edging, Trimming

Chemical Composition

C	Si	Mn	Cr	S	P
0.95～1.20	≤1.0	≤1.0	16.0～18.0	≤ 0.03	≤ 0.04

Mechanical Properties

Tensile Strength Kb (MPa)	Yield Strength σ0.2 (MPa)	Elongation D5 (%)	Hardness
≥560	≥205	≥18	≤250HB

Physical Performance

Density(g/cm³)	Modulus of Elasticity(Gpa)	Coefficient of Thermal Expansion(10^-6/°C)	Coefficient of Thermal Conductivity(W/m*K)	Resistivity(ΜΩ. cm)
7.60	200	10.1	24.2	360