310S Stainless Steel Bar

310S is an austenitic stainless steel that combines excellent high temperature performance with good ductility and weldability. It is usually used for high temperature applications because its high chromium and nickel content provides solid corrosion resistance, excellent oxidation resistance and excellent strength at temperatures up to 2100 °F. Due to its high chromium and nickel content, it is superior to 304 or 309 stainless steel in most environments.

Classification :

Stainless Steel Bar

+86-19953173540

admin@szcnsteel.com

E-mail

310S Stainless Steel Bar Description

Product Parameters

Product Name		310S Stainless Steel Bar
Type		Steel Bar
Outer Diameter	Round Bar	4mm-500mm
	Hexagon Bar	18mm-57mm (11/16″ to 2-3/4″)
	Square Bar	18mm-47mm (11/16″ to 1-3/4″)
	Flat Steel	1/2 "to 10", Thickness: 2mm-150mm, Can provide customized
Length		1-6 meters, Length can be customized
Standard		ASTM, AISI, JIS, GB, DIN, EN, etc.
Surface		Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc.
Scope of Application		Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc.

Chemical Composition

C	Si	Mn	Cr	Ni	S	P
≤ 0.08	≤1.0	≤ 2.0	24.0～26.0	19.0～22.0	≤ 0.03	≤ 0.045

Mechanical Properties

Tensile Strength Kb (MPa)	Yield Strength σ0.2 (MPa)	Elongation D5 (%)	Hardness
≥520	≥205	≥40	≤ 217HB;≤ 95HRB

Physical Performance

Density(g/cm³)	Modulus of Elasticity(Gpa)	Coefficient of Thermal Expansion(10^-6/°C)	Coefficient of Thermal Conductivity(W/m*K)	Resistivity(ΜΩ. cm)
9.01	200	14.4	13.8	94